This Article Figures Only Full Text Full Text (PDF) Alert me when this article is cited Alert me if a correction is posted Citation Map Services Email this article to a friend Similar articles in this journal Similar articles in Web of Science Alert me to new issues of the journal Download to citation manager Citing Articles Citing Articles via Google Scholar Google Scholar Articles by Hassan, M. S. Articles by Baioumy, H. M. Search for Related Content GeoRef GeoRef Citation

STRUCTURAL AND CHEMICAL ALTERATION OF GLAUCONITE UNDER PROGRESSIVE ACID TREATMENT

Central Metallurgical R & D Institute, PO Box 87 Helwan, Cairo, Egypt

^* E-mail address of corresponding author: mervathassan{at}hotmail.com

Boiling glauconite from the El-Gideda area of Egypt in different concentrations of HCl and H₂SO₄ for different periods led to a modified structure. Treatment resulted in progressive destruction of the structure, leaving X-ray amorphous silica and only relics of the original mineral. The glauconitic material was modified structurally in order to increase its adsorption activity. The glauconite was evaluated in terms of mineralogy, chemistry, morphology, structural modification, octahedral cation leaching rate, surface area and cation exchange capacity using X-ray diffraction, infrared spectroscopy, X-ray fluorescence, scanning electron microscopy and surface area analysis. The ratio of extracted octahedral cations to the total octahedral cations in the untreated glauconite was taken as a measure of octahedral sheet decomposition. A progressive decrease in crystallinity and the formation of X-ray amorphous silica Si–O vibration bands at 1100, 800 and 494 cm^–1 accompanied octahedral cation depletion. Acid activation using 2 M and 4 M HCl for 6 h destroyed 30% and 61% of the octahedral sheet, respectively. In contrast, similar treatment using 2.9 and 5.5 M H₂SO₄ destroyed 48% and 93% of the octahedral sheet, respectively. Depending on the extent of cation depletion, the 4 M HCl product surface areas were as high as 259 m²/g, whereas the surface area of the 5.5 MH₂SO₄ product was only 63 m²/g. The progressive increase in surface area was due to glauconite morphology alteration. Acid-induced dissolution of Al, Fe, Mg cations from octahedral sheet edges led to a wedge-like splitting of the glauconite crystals, mesopore creation, and greater access to interlayer galleries.

Key Words: • El-Gideda • Egypt • Glauconite • Structural Modification